TC-80DP is a high abrasion resistance and strength
1.
High Flexural Strengh 220 Mpa ~ 360 Mpa
High Tensile and Impact Strength.
Nontoxic, Biocompatible.
For dental(C&B) and laminate.
1
2.
Comparison to general C&BName
Tera Harz (TC-80DP)
(Graphy)
Varseo Smile Crown plu
s
(BEGO)
C&B MFH
CrownTec
(NextDent)
(Saremco)
Color
A1,A2,A3
(The rest use colorants)
A1,A2,A3
A1,A2,A3
Permanent
Restorations
Viscosity
2,200 cPS
2,500 ~ 6,000 cPS
-
-
Bi-axial Flexural
Strength
≥ 360 MPa
Flexural strength
220 MPa
116 Mpa
107 MPa
130 MPa
Flexural modulus
4,500 MPa
4,090 MPa
-
4,000 MPa
Elongation
<10 %
<4 %
<4 %
<4 %
Wavelength
405 nm
405 nm
405 nm
405 nm
2
A1,A2,A3
3.
Clinical CasesAll-on-6
Graphy TC 80DP
3
4.
Clinical Cases4
5.
Clinical CasesImmediate implant placement & Loading
5
6.
Clinical CasesIntra Oral Scan : 5 min
Inlay Design : 5~10 min
Setting time : 15~20 min
3D Printing (100um) : 15~20 min
Density Curing time : 10 min